Conductive Carbon Black Polypropylene Compounds For Hollow Sheet

Dongguan SUGO Plastics Technology Co., Ltd.
Trust Seal
Verified Supplier
Credit Check
Supplier Assessment

Conductive Carbon Black Polypropylene Compounds For Hollow Sheet

Brand Name : SUGO

Model Number : K2103

Certification : ISO9001:2008

Place of Origin : CHINA

MOQ : 200 kgs

Price : USD/KG

Payment Terms : L/C, T/T

Supply Ability : 5000 tons Monthly

Delivery Time : 3-7 days

Packaging Details : 25Kg/Bag, 40 Bags/Pallet

Surface Resistivity : 1*10E3~E5 Ohms

Volume Resistivity : 1*10E3~E5 Ohms

Color : Black

Model # : K2103

Style : Compounds

Application1 : PP Hollow Sheet For Container of Sensitive Electronics

Application2 : PP IC Tray, PP PCBA Tray

Density : 1.041 g/cm³

Melt Flow Rate (200℃/5.0kg) : 7.6 g/10min (

Flow Shrinkage : 1.46%

Tensile Strength : 30 Mpa

Bending Modulus : 1725 Mpa

Bending Strength (break) : 55 Mpa

Elongation : 12%

Izod Dent Impact Strength (3.2mm) : 2.3 Kgf/cm.cm

Distortion Temperature : 70 °C

Contact Now


Conductive Propylene Carbon Black Compounds Used For PP Hollow Sheet


As we know common plastics before modified is an insulator, the static electricity caused by friction
can not be discharged naturally until a conductor's lead, but electricity's discharge will cause devastating
damage on inner circuit, this is why our modified plastics are invented. with some conductive filler, the
with different filling percent of conductive master batch the surface or volume resistivity can be adjusted
from 10E3-E10, and can protect electronic parts away from discharge of static electricity.
Model No. K2103 PP conductive compunds solve the above problem perfectly by offering a surface re-
sistivity of 10E3~E4 Ohms.
Here is more technical information for reference:
Physical PropertyNominal ValueUnitTest Method
Density1.041g/cm³ASTMD792
MFR(300℃/10.0kg)7.6g/10minASTMD1238
Molding Shrinkage1.46%ASTMD955
Mechanical PropertyNominal ValueUnitTest Method
Tensile Strength30MPaASTMD638
Flexural Modulus1725MPaASTMD790
Flexural Strength55MPaASTMD790
Elongation12%ASTMD638
ImpactNominal ValueUnitTest Method
Izod ( 3.2mm)2.3Kgf/cm.cmASTMD256
Notched Izod impact( 3.2mm)
ThermalNominal ValueUnitTest Method
(1.82MPa)70°CASTMD648
Deflection temperature under load (1.82Mpa)
Electrical PropertyNominal ValueUnitTest Method
Surface ResistivityE3-E4ohm/sqASTMD257
Injection(Metric) Nominal Value 
Drying Temperature100°C
Drying Time 4.0hr 
Rear Temperature170~180°C
Middle Temperature180~190°C 
Front Temperature200~210°C 

This model's perfection application is made to PP Hollow Sheet and finally made to containers for storing

and transporting the sensitive electronic parts:




Please contact us for more information and cooperation.


Thank you!



Product Tags:

Conductive PP Compounds

      

Carbon Black PP Compounds

      

Conductive Polypropylene Compound

      
Best Conductive Carbon Black Polypropylene Compounds For Hollow Sheet wholesale

Conductive Carbon Black Polypropylene Compounds For Hollow Sheet Images

Inquiry Cart 0
Send your message to this supplier
 
*From:
*To: Dongguan SUGO Plastics Technology Co., Ltd.
*Subject:
*Message:
Characters Remaining: (0/3000)